Material |
Description |
Al2O3 |
Tablets/Granules, Fused or Sintered, T=200-5000nm, n=1.63 at 500nm |
BaF2 |
Tablets, T=250-15000nm, IR coatings, n=1.48 at 500nm |
CaF2 |
Tablets, T=150-12000nm, n= 1.3 at 500nm |
CeO2 |
Tablets, AR coatings for UV-VIS. T=400-14,000nm. n=2.08 at 500nm |
Na5Al3F14 |
Tablets, T=250-14000nm, n=1.3 at 500nm |
Na3AlF6 |
Tablets, T= 250-14000nm, n=1.33 at 500nm |
HfO2 |
UV Grade/Tabs/Granules, Zr <0.5%, T=230-7000nm, n=1.95 at 500nm |
ITO |
Tablets,T=400-1000nm, |
PbF2 |
Tablets, T=250-16µm, n=1.75 at 500nm |
LiF |
Granules, T=100-7000nm, n=1.4 at 550nm |
MgF2 |
Tablets/Granules, T=150-7000nm, n=1.37 at 550nm |
MgO |
Tablets/Granules,T=200-8000nm, n=1.7 at 500nm |
MgAl2O4 |
Tablets/Granules |
Nb2O5 |
Tablets/Granules |
SiO2 |
Granules,T=170-2000nm, n=1.46 at 500nm |
SiO |
Granules, T=600-8000nm, n=1.55 at 550nm |
Ta2O5 |
Tablets/Black, T=350-7000nm, n=2.1 at 500nm |
TiO2 |
Tablets/Black/White, T=400-12000nm, n=2.3 at 550nm |
Ti2O3 |
Tablets, T=400-12000nm, n=2.35 at 500nm |
Ti3O5 |
Tablets, T=400-12000nm, n=2.35 at 500nm |
TiO |
Granules, T=400-1200nm, n=2.35 at 500nm |
Y2O3 |
Tablets/Granules, T=300-8000nm, n=1.9 at 550nm |
ZnS |
Tablets, T=400-14000nm, n=2.39 at 550nm |
ZrO2 |
Tablets/Granules, T=300-7000nm, n=2.05 at 500nm |
Optima 1 |
ZrO2/TiO2, T= 350-7000nm, n=2.1 at 550nm |
Optima 2 |
TiO2/Pr6O11, T= 400-7000nm, n=2.1 at 550nm |
Optima 3 |
Tablets, thick, low stress IR coatings, ThF 4 replacement |
Optima 4 |
ZrO2/Ta2O5, T=370-7000nm, n=2.05 at 500nm |
Optima 5 |
TiO2/Ta2O5, T=400-7000nm, n=2.15 at 500nm |